Abstract
Abstract
Hot stamping is a technique to produce ultra high strength automobile components. The common material used in hot stamping process is coated and/or uncoated 22MnB5 boron alloyed steel. Ferritic‐pearlitic microstructure in as‐delivered sheets is transformed to fully lath martensitic after hot stamping. In the present research, hot stamping under water or nitrogen cooling media was investigated using different boron alloyed steel grades. Microstructural analyses, linear and surface hardness profiling as well as tensile tests of hot stamped samples were performed. Various microstructures of fully bainitic and/or fully martensitic were produced. The resulting microstructures provided yield strengths of 650–1370 MPa and tensile strengths of 850–2000 MPa. There is an optimum carbon equivalent content for which the highest formability index value, UTS × A25, is achieved. Using a nitrogen cooled punch resulted in higher yield strength without significant changes in ultimate tensile strength. It is concluded that a wide range of B‐bearing steels having an extended carbon equivalent range with an acceptable formability index value can be used by increasing the cooling rate in the die assembly.