Abstract
Abstract
Two creep resistant steels, P91 and X20, were tempered for 17520 h at 650 °C or 8760 h at 750 °C to study the growth and redistribution of carbide precipitates in martensite. On specimens annealed for a different time, yield stress at room temperature and accelerated creep rate at 580 °C were determined. With increasing yield stress in the range from 350 to 650 MPa the accelerated creep rate decreased continuously by about 2 orders of magnitude from 8·10−7 s−1 to 5·10−9 s−1. For equal yield stress, the creep rate was slightly lower for the steel P91 than for the steel X20.