Abstract
The Ce–Bi co-doped CdO electrode had a maximum specific capacitance of 252.7 F g
−1
at a current density of 0.8 A g
−1
, with a decrease in charge transfer resistance (
R
ct
) from 0.41 to 0.26 Ω.
Ikram Ahmad, Muzammal Aslam, A. F. A. Kadir, Sajjad Gull, Ali Mujtaba, Tahira Ramzan, Ahmed Sheraz
Abstract
Authors
Institutions
No ROR-resolved institution is linked to this work yet.
Provenance
crossref
Confidence 100%
pubmed
Confidence 98%
No local reference links have been materialized yet.
No local citing links have been materialized yet.
10.1049/mna2.12148
10.1049/mna2.12148 · 2022
10.1002/9781119741503.ch7
10.1002/9781119741503.ch7 · 2021
Unresolved referenced work
2023
10.1016/j.energy.2022.123617
10.1016/j.energy.2022.123617 · 2022
10.1039/c9nr07008g
10.1039/c9nr07008g · 2020
10.1016/j.mssp.2026.110993
10.1016/j.mssp.2026.110993 · 2026
10.1007/s11581-025-06393-z
10.1007/s11581-025-06393-z · 2025
10.1039/d6ra05413g
10.1039/d6ra05413g · 2026
10.1016/j.vacuum.2019.01.042
10.1016/j.vacuum.2019.01.042 · 2019
10.1007/s10904-024-03523-4
10.1007/s10904-024-03523-4 · 2025
10.1016/j.jallcom.2022.168462
10.1016/j.jallcom.2022.168462 · 2023
10.1016/j.ijhydene.2022.09.047
europepmc
Confidence 96%
unpaywall
Confidence 95%
doaj
Confidence 92%
datacite
Confidence 0%
10.1016/j.ijhydene.2022.09.047 · 2022
10.1016/j.jallcom.2021.160885
10.1016/j.jallcom.2021.160885 · 2021
10.1016/j.ceramint.2021.07.259
10.1016/j.ceramint.2021.07.259 · 2021
Unresolved referenced work
2022
10.1016/j.mseb.2025.118455
10.1016/j.mseb.2025.118455 · 2025
10.1039/d5ra08524a
10.1039/d5ra08524a · 2025
10.1039/c9ce01556f
10.1039/c9ce01556f · 2020
10.1016/j.cscee.2024.101038
10.1016/j.cscee.2024.101038 · 2025
10.1016/j.electacta.2025.145963
10.1016/j.electacta.2025.145963 · 2025
10.1016/j.ceramint.2024.12.431
10.1016/j.ceramint.2024.12.431 · 2025
10.1016/j.talanta.2024.127427
10.1016/j.talanta.2024.127427 · 2025
10.1016/j.carbon.2025.120028
10.1016/j.carbon.2025.120028 · 2025
10.1016/j.ceramint.2025.02.192
10.1016/j.ceramint.2025.02.192 · 2025
Unresolved referenced work
2016
10.1016/j.mseb.2022.115754
10.1016/j.mseb.2022.115754 · 2022
10.1007/s00339-024-07548-x
10.1007/s00339-024-07548-x · 2024
10.1016/j.molstruc.2014.02.056
10.1016/j.molstruc.2014.02.056 · 2014
10.1016/j.solidstatesciences.2012.01.019
10.1016/j.solidstatesciences.2012.01.019 · 2012
10.1016/j.solener.2026.114892
10.1016/j.solener.2026.114892 · 2026
10.1016/j.cej.2023.144574
10.1016/j.cej.2023.144574 · 2023
10.1088/1361-6404/aab598
10.1088/1361-6404/aab598 · 2018
10.1016/j.ceramint.2021.09.207
10.1016/j.ceramint.2021.09.207 · 2022
10.1039/d1ee00166c
10.1039/d1ee00166c · 2021
10.1007/s12668-025-01996-2
10.1007/s12668-025-01996-2 · 2025
10.3390/coatings12020215
10.3390/coatings12020215 · 2022
10.1016/j.apsusc.2024.159746
10.1016/j.apsusc.2024.159746 · 2024
10.1007/s12668-023-01158-2
10.1007/s12668-023-01158-2 · 2023
10.1016/j.est.2023.109539
10.1016/j.est.2023.109539 · 2023
10.3389/fchem.2025.1636683
10.3389/fchem.2025.1636683 · 2025
10.1002/ente.202501583
10.1002/ente.202501583 · doi-reference
10.1021/acsomega.3c02261
10.1021/acsomega.3c02261 · doi-reference
10.1016/j.est.2025.119346
10.1016/j.est.2025.119346 · doi-reference
10.1039/d5na00491h
10.1039/d5na00491h · doi-reference
10.1016/j.jics.2025.101709
10.1016/j.jics.2025.101709 · doi-reference
10.1088/0957-4484/22/2/025501
10.1088/0957-4484/22/2/025501 · doi-reference
10.1109/tpel.2016.2608278
10.1109/tpel.2016.2608278 · doi-reference
10.1007/s41918-022-00155-5
10.1007/s41918-022-00155-5 · doi-reference
10.1002/adfm.202101868
10.1002/adfm.202101868 · doi-reference
10.1016/j.diamond.2025.112390
10.1016/j.diamond.2025.112390 · doi-reference
10.1016/j.matpr.2023.05.175
10.1016/j.matpr.2023.05.175 · doi-reference
10.1140/epjp/s13360-025-06901-0
10.1140/epjp/s13360-025-06901-0 · doi-reference