Abstract
Mg2Ni0.8Cr0.2-x wt.% CoO/Al2O3 (x=0.5, 1, 2 and 3) composites were prepared by mechanically milling sintered Mg2Ni0.8Cr0.2 alloy and CoO/Al2O3 compound for 45 h. The addition of CoO/Al2O3 compound resulted in the good kinetics properties of hydriding/dehydriding reaction of the composites. The composite with 1.0 wt.% CoO/Al2O3 catalyst could reach the maximum hydrogen absorption capacity (2.9 wt.%) within 5 min at 393 K under H2 pressure of 4 MPa, and can desorb rapidly at 493 K. The decomposition and synthesis of hydrogen molecule on Mg2Ni0.8Cr0.2 alloy surface was promoted by addition of CoO/Al2O3 catalyst. In addition, the formation of metallic Ni particles, strain and defects during the ball milling process also resulted in the improved hydrogenation performance of Mg2Ni-based alloys.