Sulfur dioxide adsorption by Iron Oxide Nanoparticles@Clinoptilolite/HCl

Introduction: The purpose of this study was to investigate and compare   the effect of iron oxide nanoparticles on the adsorption of sulfur dioxide by modified zeolite with hydrochloric acid. In this investigation was used modi- fied zeolite with HCl with and without iron oxide nanoparticles (Iron Oxide Nanoparticles@Clinoptilolite/HCl) as adsorbent. Materials and methods: Structural characteristics, chemical composition and specific surface area of adsorbent were determined using the FTIR, FE- SEM, EDX, Mapping, XRD, XRF and BET techniques. Glass cylinder filled with zeolite seeds and SO2 cylinder balanced with N2 gas was used for experi- ments. It was evaluated factors affecting SO2  uptake process including tem- perature and contact time, also thermodynamics and kinetics of adsorption. Sulfur dioxide adsorption of real sample was taken with both adsorbents. Results: Adsorption efficiency of SO2 in the synthetic and actual sample were %82.8±5.5 and %67.2±7.21 respectively, by modified zeolite with HCl and iron oxide nanoparticles in the optimum conditions of temperature of 25 °C and duration 28.5 min. As well as, removal percentage average was obtained in the synthetic and actual sample %46.1±4.34 and %35.8±5.85 respectively, by modified zeolite with HCl without nanoparticles in optimum condition of temperature of 25 °C and contact time of 20.5 min.The results showed that SO2  adsorption is an exothermic and spontaneous process and adsorption ki- netics of sulfur dioxide by both adsorbent is more consistent  Pseudo-second order kinetics model. Conclusion: The use of iron oxide nanoparticles on the zeolite can increase SO2 removal efficiency from the gas phase.